VERBATIM 3D Printer Filament PET-G 1.75mm, 327m, 1kg transparent
VERBATIM 3D Printer Filament PET-G 1.75mm, 327m, 1kg transparent
544 Kč
449 Kč bez DPH
Dostupnost: Skladem v eshopu
Part no.: 55051
Kód produktu: 73898392
Výrobce: Verbatim
Popis produktu
Strong, high clarity, odour neutral and easy-to-print filament
High impact strength
Excellent flexibility
Almost no warping or shrinkage
Hydrophobic (does not absorb water)
Food packaging grade pellets used
Main applications: Concept modelling for mechanics, medical, food containers, transparent objects.
TECHNICAL SPECIFICATIONS
Diameter
1.75 mm ± 0.05 mm
Roundness
>95%
RAL
N/A
Weight
1000 g
Color
transparent
MATERIAL PROPERTIES
Specific gravity
1.27g/cc (Test method: ISO 1183)
MFR 190°C/2.16 kg
6.4 gr/10 min (Test method: ISO 1133)
Tensile strength at yield
50 mPa
Strain at yield
5% (Test method: ISO 527)
Strain at break
23% (Test method: ISO 527)
Tensile modulus
2020 MPa (Test method: ISO 527)
Flexural modulus
2050 MPa (Test method: ISO 178)
Flexural strength
69 MPa (Test method: ISO 178)
Impact strength - Charpy method 23°C
8.1 kJ/m2 (Test method: ISO 179)
Rockwell Hardness
105 (Test method: ASTM D785)
Moisture absorption
1104 ppm (Test method: ISO 62)
Printing temperature
240±10°C
Heat deflection temperature
70°C (Test metod: ASTM 648)
Transparency
90% (Test method: ASTM D1003)
Popis produktu
FeaturesStrong, high clarity, odour neutral and easy-to-print filament
High impact strength
Excellent flexibility
Almost no warping or shrinkage
Hydrophobic (does not absorb water)
Food packaging grade pellets used
Main applications: Concept modelling for mechanics, medical, food containers, transparent objects.
TECHNICAL SPECIFICATIONS
Diameter
1.75 mm ± 0.05 mm
Roundness
>95%
RAL
N/A
Weight
1000 g
Color
transparent
MATERIAL PROPERTIES
Specific gravity
1.27g/cc (Test method: ISO 1183)
MFR 190°C/2.16 kg
6.4 gr/10 min (Test method: ISO 1133)
Tensile strength at yield
50 mPa
Strain at yield
5% (Test method: ISO 527)
Strain at break
23% (Test method: ISO 527)
Tensile modulus
2020 MPa (Test method: ISO 527)
Flexural modulus
2050 MPa (Test method: ISO 178)
Flexural strength
69 MPa (Test method: ISO 178)
Impact strength - Charpy method 23°C
8.1 kJ/m2 (Test method: ISO 179)
Rockwell Hardness
105 (Test method: ASTM D785)
Moisture absorption
1104 ppm (Test method: ISO 62)
Printing temperature
240±10°C
Heat deflection temperature
70°C (Test metod: ASTM 648)
Transparency
90% (Test method: ASTM D1003)